Honeycomb Structures of TiO2-modified Hydroxyapatite Composite for Microbial Filtration Application

Naruporn Monmaturapoj, Witoon Thepsuwan, Suda Wanakitti, Charusporn Mongkolkachit, Katanchalee Mai-ngam, Sawinee Ngernpimai, Wattana Klinsukhon and Chureerat Prahsarn

Honeycomb structures of TiO2-modified hydroxyapatite composite (HA/TiO2) were fabricated using extrusion technique. The mixture formulations of HA/TiO2 extrusion pastes (S1-S4) were investigated to optimize the process. The filtering effectiveness of the HA/TiO2 honeycombs was evaluated by photocatalytic activity measurement and a bactericidal test. The effects of sintering temperature and honeycomb thickness on photocatalytic and antibacterial activities were additionally studied. The S3 and S4 honeycomb samples, sintered at 650°C, exhibited a similar trend in reducing methylene blue concentration. At 800°C, the S3 honeycomb sample showed a slightly faster reduction in methylene blue concentration compared to the S4 honeycomb. Honeycomb samples of 2 and 5 cm in thickness showed significantly greater photocatalytic activity than that of 1 cm such that methylene blue concentrations rapidly decreased after UV exposure for 24 hours. The S3 and S4 honeycomb samples also exhibited decomposition of both gram-negative E. coli and gram-positive S. aureus. Approximately 50% of gram-positive S. aureus and gramnegative E. coli were decomposed by the honeycombs in the sample-thickness dependent manner after 2 hours of UV exposure. Low survival ratios of bacteria (5% - 10%) were observed after 6 hours of UV exposure and the 2 mm and 5 mm thick honeycomb samples showed the greatest and most similar antibacterial activities.